TiO2/氮掺杂碳纳米管复合材料的制备及光催化性能的提高

2014-5-22 9:13:46

汪玲玲,沈龙,李奕怀,朱路平,沈娇雯,王利军
(上海第二工业大学城市建设与环境工程学院)
 
摘要:采用简易的水热合成法制备了TiO2/氮掺杂碳纳米管复合材料。利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电镜(TEM)和热重-差热分析(TG-DSC)等对样品进行了详细的表征。结果表明,粒径约为7nm的TiO2纳米粒子均匀的负载在氮掺杂碳纳米管表面。以甲基橙作为模型污染物,研究了TiO2/氮掺杂碳纳米管复合材料作为光催化剂在紫外光照射下的光催化能力,结果显示TiO2/氮掺杂碳纳米管复合材料对环境污染物具有良好的降解能力。但是氮掺杂碳纳米管和TiO2的机械混合物比单纯的TiO2光催化性能要差。此外,TiO2/氮掺杂碳纳米管复合材料的光催化性能优越于单纯的TiO2和TiO2/碳纳米管复合材料的性能,这是由于光生电子从TiO2转移到了氮掺杂碳纳米管从而有效得抑制了电子和空穴的复合。
 
Enhancement of Photocatalytic Activity on TiO2-nitrogen Doped Carbon Nanotubes Nanocomposites
Lingling Wanga, Long Shenb, Yihuai Lia, Luping Zhua, Jiaowen Shena, Lijun Wanga*
aSchool of Urban Development and Environment Engineering, Shanghai Second Polytechnic University, 2360 Jinhai Road, Shanghai, 201209, P. R. China.
bShanghai Shanshan Technology Co., Ltd., 3158 Jinhai Road, Shanghai,   
 
Abstract
TiO2-nitrogen doped carbon nanotubes (TiO2-CNx) nanocomposites are successfully synthesized via a facile hydrothermal method. The prepared photocatalysts were systematically characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and thermogravimetric and differential scanning calorimetry analyses (TGA-DSC). The results show that the TiO2 nanoparticles with a narrow size of 7 nm are uniformly deposited on CNx. The photocatalytic activity of the nanocomposite was studied using methyl orange (MO) as a model organic pollutant. The experimental results revealed that the strong linkage between the CNx and TiO2 played a significant role in improving photocatalytic activity. However, the mechanical process for CNx and TiO2 mixtures showed lower activity than neat TiO2. Moreover, TiO2-CNx nanocomposites exhibit much higher photocatalytic activity than that of neat TiO2 and TiO2-CNTs nanocomposites. The improved photodegradation performances are attributed to the suppressed recombination of electrons and holes caused by the effective transfer of photogenerated electrons from TiO2 to CNx.
 
1. Introduction
Photocatalysis has been widely applied as a technique of destruction of organic pollutants due to its high performance, low cost, nontoxicity, stability and availability [1,2]. Titanium dioxide (TiO2), a semiconductor with direct bandgap of 3.2 eV, has excellent photocatalytic properties and chemical stability, and it is an environmentally friendly and abundant substance [3,4]. However, a major limitation to achieve high photocatalytic efficiency is the quick recombination of photo-generated charge carries [5]. Recombination has faster kinetics than surface redox reactions and greatly reduces the quantum efficiency of photocatalysis. Therefore, currently a particularly attractive option is to design and develop hybrid materials based on TiO2 to solve this problem.
Recently, carbon-based nanomaterials, such as carbon nanotubes (CNTs) and graphene, have been reported as the hybrid component to be incorporated into TiO2 due to their unique electrical properties, superior chemical stability and good conductivity. The common approaches to synthesize TiO2-CNTs composites include sol-gel method [6,7], chemical vapor deposition (CVD) [8,9], electrospinning [10], and so on. Various structural forms of titania-carbon nanotubes photocatalysts have been prepared, such as TiO2 nanoparticles on CNTs [11], TiO2 layer coating on aligned CNTs arrays [12], CNTs incorporating into the TiO2 film [13], TiO2 layer coating on CNTs [14] and low loading amounts of CNTs embedded inside mesoporous TiO2 aggregates[15]. Cong et al. [16] have prepared uniform and fine well-dispersed carbon-doped TiO2 coating on multiwalled carbon nanotubes by oxidation of titanium carbide (TiC) coated CNTs, and the prepared carbon-doped TiO2 coating on CNTs shows a higher visible light photocatalytic activity.
However, to fabricate the TiO2-CNTs composites, the CNTs required a pretreatment process to modify their inert surface nature via harsh processes for activation by refluxing in concentrated acids, which destroys the π conjugation and reduces the conductance of the CNTs base[17]. Unfavorably, the harsh process would risk CNTs to some damages in their inherent properties. To bypass the drawbacks suffered by CNTs, employing CNx without requiring any pre-treatment to composite with the functional materials directly is a promising method, because the nitrogen atoms on the surface of the CNTs modifies the adsorption strength of the nanotubes towards foreign elements. Moreover, nitrogen atoms in the framework of CNx will form chemically active points which are available for metal or metallic oxide nanoparticles anchoring. Ghosh and coworkers [17] prepared ZnO/CNx composites via a simple wet-chemical method and studied their field emission performance. CNx decorated with CeO2 and SnO2 nanoparticles showed greater activity and sensitivity than the conventional CNT-based composites for NO electrooxidation[18].
In this work, according to the unique properties of CNx, we have synthesized TiO2-CNx nanocomposites with different weight ratios via a facile hydrothermal method. The resulting materials were well characterized for their physicochemical properties, structural features, as well as potential applications to the photodegradation of MO.
 
2. Experimental
2.1. Synthesis of TiO2-CNx
Following the procedures reported previously[19], CNx was synthesized using diethylamine as the carbon and nitrogen source. The purification process for CNx was as follows: CNx was firstly washed three times by 20% HF solution, then soaked in 20% HF solution overnight, gathered by filtration and finally dried at 80 ℃ for 2 h.
TiO2-CNx nanocomposites were prepared using a hydrothermal synthesis method. CNx was added to provide a weight ratio of TiO2 over CNx in the range from 5% to 20%, indicated with X wt% TiO2-CNx. CNx was initially dispersed into a 30 mL solution containing 2.7 mL water and 27.3 mL isopropanol, the suspension was treated by sonication overnight. Then the titanium precursor solution, 3.41 mL titanium isopropoxide in 18 mL isopropanol was added dropwise into the CNx suspension under vigorous stirring. The mixture was left at room temperature under stirring for 2 h to complete the hydrolysis reaction. The mixed solution was then transferred into a teflon lined stainless-steel autoclave (50 mL capacity). The autoclave was maintained at 140 ℃ for 24 h, then cooled down to room temperature. The resulting solid was washed with ethanol and deionized water, gathered by filtration, and subsequently dried at 80 ℃ overnight. The TiO2-CNx solids were ground into powder and stored in a dessicator for further usage. For comparison, TiO2-CNTs composites were synthesized using the similar procedures besides CNTs pretreated in concentrated HNO3 at 140 ℃ for 14 h, and neat TiO2 sample was synthesized without adding CNTs.
2.2. Characterization
The bare CNx and the composites were characterized by a wide range of analytical techniques. The degree of crystallinity of the TiO2-CNx composites was characterized by powder X-ray diffraction (XRD). The XRD patterns with diffraction intensity versus 2θ were recorded in a Bruker D8 ADVANCE instrument with Cu-Ka radiation (λ=1.5418 Å) from 20 o to 70 o at a scanning speed of 2 o/min. X-ray tube voltage and current were set at 40 kV and 40 mA, respectively. Thermogravimetric and differential scanning calorimetry analyses (TGA-DSC) were performed by a Netzsch STA-449C analyzer with a heating rate of 10 ℃/min and an air flow rate of 100 mL/min. Scanning electron microscopy (SEM) was carried out on Hitachi S-4800 with an acceleration voltage of 5 kV. Transmission electron microscopy (TEM) was carried out on JEOL-JEM-1005 at 200 kV. The specimens for SEM and TEM imaging were prepared by suspending solid samples in ethanol with 15 min ultrasonication and placing a drop of this mixture on a 3.05 mm diameter copper mesh, which was then dried in air.
2.3. Photodegradation of MO
The photoreactor was designed with a cylindrical quartz cell configuration and an internal light source surrounded by a quartz jacket, where MO aqueous solution completely surrounded the light source. An external cycled cooling flow of water was used to maintain the reaction temperature constant.
Photocatalytic experiments were carried out by adding 0.01 g TiO2 or TiO2-CNTs composites or TiO2-CNx composites into photoreactor containing 30 mL MO solution with an initial concentration of 15 mg/L. The mixture was stirred for 30 min in the dark to favor the adsorption equilibration, then the stirred suspensions were illuminated with a 300 W high-pressure mercury lamp 10 cm high over the solution. The solution was stirred continuously during the photocatalytic reaction. The concentration of MO was analyzed by recording the absorption band maximum at 464 nm in the absorption spectra, using Shimadzu UV-2550 spectrophotometer.
 
3. Results and discussion
The XRD patterns of the bare CNx and TiO2-CNx nanocomposites are shown in Figure 1. The main peaks at 26.1 o and 42.6 o corresponded to the (002) and (100) reflections of CNx respectively (JCPDS 41-1487),which indicated that the employed CNx were highly graphitized (Figure 1a). It is obvious that the TiO2-CNx nanocomposites show the same characteristic diffraction peaks referred to anatase TiO2 (JCPDS No.21-1272). The characteristic peaks at 2θ of 25.3, 37.8, 48.0, 53.9, 55.1 and 62.7 ° can be indexed to (101), (004), (200), (105), (211) and (204) crystal planes of anatase TiO2, respectively. Notably, no typical diffraction peaks belonging to the separate CNx are observed in the TiO2-CNx nanocomposites. The reason can be ascribed to the fact that the main characteristic peak of CNx at 26.1 ° might be shielded by the main peak of anatase TiO2 at 25.3 °.
Figures 2 and 3 show the SEM and TEM images of bare CNx and TiO2-CNx composites. CNx with relatively outer diameter (30~60 nm) were obtained, and the nanomaterial has a bamboo-like morphology with a clear, smooth surface. It is clearly seen that for TiO2-CNx nanocomposites, the TiO2 nanoparticles are almost uniformly deposited on the surface of CNx. The more weight ratio of TiO2 over CNx, the more visible nanoparticles observed (Figures. 2b, 2c and 2d).  Figure 3b is TEM image of an individual CNx fully coated with TiO2 nanoparticles. The bamboo-like morphology of CNx can be also clearly observed, and its surface is entirely and homogeneously covered by TiO2 nanoparticles. There are no clear boundary and vacant space between the TiO2 coating and CNx substrate. The nanoparticles covered on the CNx show clear crystal lattice fringes (Figure 3c). The intimate contact between CNx and TiO2 favors the formation of junctions between the two materials, as a result, being helpful for improving the charge separation and thus the photocatalytic activity. As estimated from the TEM images, the size of TiO2 nanoparticles is about 7 nm. EDX spectrum presented in Figure 3d further determined the existence of Ti and O atoms.
TGA-DSC analysis was carried out to estimate the carbon nanotube content of the nanocomposite. The results of weight loss and heat flow as a function of temperature for TiO2-CNx nanocomposites are shown in Figure 4. For the 5 wt% and 15 wt% TiO2-CNx nanocomposites, the weight loss due to the combustion of the CNx was 93.5% and 83.8% respectively, indicating that TiO2/CNx ratios estimated from the synthesis precursors of the nanocomposites were in close agreement with the results obtained from TGA-DSC analyses. Therefore, negligible losses of CNx occurred during the composite preparation procedure. The combustion point of CNx in the 15 wt% TiO2-CNx composite was found to be 544.3 ℃, whereas CNx in 5 wt% TiO2-CNx composite could not be combusted until approximately 647.6 ℃. The combustion temperature shift between different TiO2/CNx ratios may be ascribed to the following two reasons (i) more amount of TiO2 grafted on the sidewall of CNx may provide more oxygen required by the combustion of CNx. (ii) more amount of TiO2 restrain the heat transfer creating localized hot spots, facilitating the oxidation of carbon.
Figure 5 shows the results of the decomposition of MO under irradiation, in the presence of neat TiO2, TiO2-CNTs and TiO2-CNx nanocomposites with different weight ratios. Control experiments showed that UV irradiation with no catalyst and catalyst (composite or bare CNx) without irradiation could not degrade MO dye solutions. When TiO2 photocatalyst is used, the degradation efficiency is calculated to be 82.4% at 110 min. When CNTs is introduced, the degradation efficiency is increased to 91.1% for 10 wt% TiO2-CNTs composites and reaches the maximum value of 99.6% for 20 wt% TiO2-CNx composites at 110 min. It is noteworthy that TiO2-CNx composites show superior activity to TiO2-CNTs composites with the same TiO2 weight ratio. With the reaction time at 110 min, the MO degradation efficiency of 10 wt% TiO2-CNTs catalysts is about 91.1%. However, the value of 10 wt% TiO2-CNx is 98.2%. Hence, TiO2-CNx is an excellent photocatalyst in our experiment.
It has been reported that high adsorption capacities of photocatalysts can lead to the rapid diffusion of MO molecules from solution to the surface of photocatalysts and thus improve photocatalytic performances[20]. Figure 6 shows the remaining fraction of MO (C/C0) in solution during adsorption for 60min in dark by neat TiO2, TiO2-CNTs composites and TiO2-CNx composites. It is obvious three photocatalysts exhibited adsorption capacities for MO molecules in the following order: 10 wt% TiO2-CNx >10 wt% TiO2-CNTs> TiO2. The improved adsorption capacity of 10 wt% TiO2-CNx is attributed to its larger specific surface area of 150.25 m2/g than these of 10 wt% TiO2-CNTs (128.26 m2/g) and neat TiO2 (85.49 m2/g). It is noteworthy that the concentration of MO molecules show neglible change after 30min,indicating the adsorption equilibration. So the adsorption is not the main reason for the improvement of photocatalytic activity in our experiment because the mixture was stirred for 30 min in advance. The enhancement of the photocatalytic performance should be mainly ascribed to the promotion of separation rate of photogenerated electron and hole by the formation of heterostructure, as shown in Figure 7.
Under UV irradiation, the valence band electrons of TiO2 can be excited to its conduction bands, giving rise to high energy electron-hole pairs. Compared with CNTs, CNx has a high degree of defects introduced by nitrogen doping [21]. When the electrons generated by TiO2 transfer into CNx, it could be used as a larger capacity container of electron in comparison with the usual CNTs. So the separation efficiency of electron-hole pairs improved, leading to the dramatically enhanced photoactivity. Moreover, compared to carbon, nitrogen has an extra electron, and from an electronic point of view it is natural to expect an excess of donors in the N-rich areas of the CNTs upon doping [22,23]. That is to say, impurities significantly enhanced the CNx metallic/conductive character [24]. Hence, the rapid transferring of electron enhanced separation rate of photogenerated electron and hole.
In order to further explore the effect of the interphase linkage, a mechanical mixture of CNx and TiO2 was prepared. The composition of the mixture was prepared with the same ratio as that in 10 wt% TiO2-CNx nanocomposites. The photocatalytic activity of the mixture photocatalyst was 76.4% at 110 min, much lower than that of 10 wt% TiO2-CNx nanocomposites (98.2%). The low activity is ascribed to CNx in the photocatalyst not being effective in trapping electrons. This lack of effectiveness prevents a decrease in recombination rate. In the mechanical mixture, it is possible that the mechanical mixture process cannot form a strong interphase between the TiO2 and the CNx. In contrast, a strong interphase was formed in TiO2-CNx composites, as evidenced by the previous analysis. Therefore, TiO2-CNx composites showed high activity. Moreover, CNx were almost inactive during MO degradation by UV light irradiation. Once CNx became incapable of bonding strongly with TiO2, they simply occupied the active sites and scattered the incident light. Therefore, the hydrothermal synthesis procedure is a critical factor in forming high-activity TiO2-CNx nanocomposites photocatalysts.
 
4. Conclusions
In this work, we have synthesized uniformly dispersed TiO2 on the surface of CNx via a hydrothermal synthesis method. The nanocomposites showed excellent photocatalytic activity compared with neat TiO2 and TiO2-CNTs. The rapid transferring of electron and high separation efficiency of electron-hole pairs lead to the dramatically enhanced photocatalytic activity. According to the activity and characterization results, the interphase linkage of TiO2 and CNx is a critical factor for promoting photocatalysis. A mechanical mixture cannot provide strong binding between TiO2 and CNx, thus showing decreased activity.
 
 
Acknowledgements
This work is supported by Leading Academic Discipline Project of Shanghai Municipal Education Commission (J51803), the National Science Foundation of China (NSFC, nos. 21101105 and 51174274), Innovation Program supported by Shanghai Municipal Education Commission (12ZZ195 and 13YZ134), Shanghai Educational Development Foundation and the Shanghai Municipal Education Commission (12CG66), “Shu Guang” Project supported by Shanghai Municipal Education Commission (09SG54), and Teachers in Shanghai Colleges and Universities (egd11008 and ZZegd12003).
 
References
[1] Y. Wang, and C. S .Hong, “Effect of hydrogen peroxide photo mineralization of 2-chlorobiphenyls: the role of O2,Water Research, vol. 34, no. 1, pp. 2791-2797, 2000.
[2] K. Tanaka, K. Padermpole, and T. Hisanaga, “Photocatalytic degradation of commercial azo dyes,” Water Research, vol. 34, no. 1, pp. 327-333, 2000.
[3] A. Fujishima, T. N. Rao, and D. A. Tryk, “Titanium dioxide photocatalysis,” Journal of Photochemistry and Photobiology C: Photochemistry Reviews, vol. 1, no. 1, pp. 1-21, 2000..
[4] Q. J. Xiang, J. G. Yu, W. G. Wang and M. Jaroniec, “Nitrogen self-doped nanosized TiO2 sheets with exposed {001} facets for enhanced visible-light photocatalytic activity,” Chemical Communications, vol. 47, pp. 6906-6908, 2011.
[5] C. Minero, and D. Vione, “A quantitative evaluation of the photocatalytic performance of TiO2 slurries,” Applied Catalysis B: Environmental, vol. 67, no. 3-4, pp. 257-269, 2006
[6] S. Wang, L. J. Ji, B. Wu, Q. M. Gong, Y. F. Zhu and J. Liang, “Influence of surface treatment on preparing nanosized TiO2 supported on carbon nanotubes,” Applied Surface Science, vol. 255, no. 2, pp. 3263-3266, 2008.
[7] W. D. Wang, P. Serp, P. Kalck, J. L. Faria, “Photocatalytic degradation of phenol on MWNT and titania composite catalysts prepared by a modified sol-gel method,” Applied Catalysis B-Environmental, vol. 56, no. 4, pp. 305-312, 2005.
[8] H. T. Yu, X. Quan, S. Chen, H. M. Zhao and Y. B. Zhang, “TiO2–carbon nanotube heterojunction arrays with a controllable thickness of TiO2 layer and their first application in photocatalysis,” Journal of Photochemistry and Photobiology A: Chemistry,vol. 200, no. 2-3, pp. 301-306, 2008
[9] H. T.Yu, X. Quan, S. Chen and H. M. Zhao, “TiO2-multiwalled carbon nanotube heterojunction arrays and their charge separation capability,” Journal of Physical Chemistry C, vol. 111, no. 35 , pp. 12987-12991, 2007
[10] S. Aryal, C. K. Kim, K. W. Kim, M. S. Khil, H. Y. Kim, “Multi-walled carbon nanotubes/TiO2 composite nanofiber by electrospinning,” Materials Science and Engineering C, vol. 28, no. 1, pp. 75-79, 2008.
[11] Y. Yao, G. Li, S. Ciston, R. M .Lueptow and K. A. Gray, “Photoreactive TiO2/Carbon nanotube composites:synthesis and reactivity,” vol. 42, no. 13, pp. 4952-4957, 2008.
[12] O. Akhavan, M. Abdolahad, Y. Abdi, S. Mohajerzadeh, “Synthesis of titania/carbon nanotube heterojunction arrays for photoinactivation of E. coli in visible light irradiation,” Carbon, vol. 47, no. 14, pp. 3280-3287, 2009.
[13] G. D. Jiang, Z. F. Lin, L. H. Zhu, Y. B. Ding and H. Q. Tang, “Preparation and photoelectrocatalytic properties of titania/carbon nanotube composite films,”  Carbon, vol. 48, no. 12, pp. 3369-3375, 2010.
[14] A. Jitianu, T. Cacciaguerra, R. Benoit, S. Delpeux, F. Béguin and S. Bonnamy, “Synthesis and characterization of carbon nanotubes-TiO2 nanocomposites,”   Carbon, vol. 42, no. 5-6, pp. 1147-1151, 2004.
[15] J. G. Yu, T. T. Ma and S. W. Liu, “Enhanced photocatalytic activity of mesoporous TiO2 aggregates by embedding carbon nanotubes as electron-transfer channel,” Physical Chemistry Chemical Physics, vol. 13, no. 8, pp. 3491-3501, 2011
[16] Y. Cong, X. K. Li, Y. Qin, Z. J. Dong, G. M.Yuan, Z. W. Cui and X. J. Lai,
Carbon-doped TiO2 coating on multiwalled carbon nanotubes with higher visible light photocatalytic activity,” Applied Catalysis B: Environmental, vol. 107, no. 1-2, pp. 128-134, 2011.
[17] K. Ghosh, M. Kumar, H. F. Wang, T. Maruyama, and Y. Ando, “Nitrogen-mediated wet-chemical formation of carbon nitride/ZnO heterojunctions for enhanced field emission,” Langmuir, vol. 26, no. 8, pp. 5527-5533, 2010.
[18] R. Zhang, L. Li, L. Chen, G. Zhang, and K. Shi, “N-doped carbon nanotubes synthesized in high yield and decorated with CeO2 and SnO2 nanoparticles,” Journal of Alloys and Compounds, vol. 509, no. 35, pp. 8620–8624, 2011.
[19] L. L. Wang, L. J. Wang, H. Y. Jin, N. C. Bing, “Nitrogen-doped carbon nanotubes with variable basicity: Preparation and catalytic properties,” Catalysis Communications, vol. 15, no. 5, pp. 78-81, 2011.
[20] R. Leary, A. Westwood, “Carbonaceous nanomaterials for the enhancement of TiO2 photocatalysis,” Carbon, vol. 49, no. 3, pp. 741-772, 2011.
[21] Y. T. Lee, N. S. Kim, S. Y. Bae et al., “Growth of vertically aligned nitrogen-doped carbon nanotubes: control of the nitrogen content over the temperature range 900-1100℃,” Journal of Physical Chemistry B, vol. 107, no. 47, pp. 12958-12963, 2003.
[22] H. S. Kang and S. Jeong, “Nitrogen doping and chirality of carbon nanotubes,” Physical Review B, vol. 70, article 233411-1, 2004.
[23] A. H. Nevidomskyy, G. Cs´anyi, and M. C. Payne, “Chemically active substitutional nitrogen impurity in carbon nanotubes,” Physical Review Letters, vol. 91, no. 10, pp. 1055021–1055024, 2003.
[24] M. Terrones, P. M. Ajayan and F. Banhart, “N-doping and coalescence of carbon nanotubes: synthesis and electronic properties,” Applied Physics A, vol. 74, no. 3, pp. 355-361, 2002.
 
 




上一篇: 引带机组的集成技术 [2014/5/16]   下一篇: 石墨烯/聚苯胺纳米复合材料作为高性能超级电容器电极材料 [2014/5/27]

 
发布评论
用户名: 密码: 验证码: 点击更换 注册


上海市科学技术委员会 | 上海市科技协会 | 中国金属学会 | 中国钢铁工业协会 | 上海有色金属协会 | 上海技术服务网 | 东方科技论坛 | 上海民间组织 | 钢材价格
版权所有 上海金属学会 (C)2007 All Rights Reserved.
地址:上海市南昌路47号3号楼3309室 电话:(021)53821027  
上海钢联电子商务有限公司 设计制作 沪ICP备06014293号